Solvay Specialty Polymers Amodel® AT-1001L Polyphthalamide (PPA)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AT-1001L Polyphthalamide (PPA).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® AT-1001L is an unreinforced, impact modified polyphthalamide (PPA) resin that exhibits exceptional impact strength at temperatures ranging from room temperature to as low as -40°F (-40°C), which suggests possible applications in ski boots and hockey skates.Features: Ductile; Good Chemical Resistance; Good Wear Resistance; Hot Water Moldability; Impact Modified; Low Temperature Impact Resistance; Low Warpage; LubricatedUses: Automotive Applications; Automotive Electronics; General Purpose; Housings; Industrial Applications; Industrial Parts; Machine/Mechanical Parts; Metal Replacement; Oil/Gas ApplicationsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Automotive Specifications ASTM D5336 PPA0110A01080 Color: NT NaturalInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Water Absorption 0.75 %

@Time 86400 sec
0.75 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.017 - 0.022 cm/cm
0.017 - 0.022 in/in
Linear Mold Shrinkage, Transverse 0.019 - 0.021 cm/cm
0.019 - 0.021 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 62.1 MPa
9010 psi
ASTM D638
Elongation at Break 30 %
30 %
ASTM D638
Elongation at Yield 6.0 %
6.0 %
ASTM D638
Tensile Modulus 1.90 GPa
276 ksi
ASTM D638
Flexural Strength 96.5 MPa
14000 psi
ASTM D790
Flexural Modulus 2.21 GPa
321 ksi
ASTM D790
Poissons Ratio 0.35
0.35
ASTM E132
Izod Impact, Notched 7.50 J/cm

@Temperature -40.0 °C
14.1 ft-lb/in

@Temperature -40.0 °F
ASTM D256
11.0 J/cm

@Temperature 23.0 °C
20.6 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Melting Point 310 °C
590 °F
DSC
Deflection Temperature at 1.8 MPa (264 psi) 120 °C

@Thickness 3.20 mm
248 °F

@Thickness 0.126 in
Annealed; ASTM D648
Processing Properties Metric English Comments
Processing Temperature 79.4 °C
175 °F
Hopper
Rear Barrel Temperature 304 - 318 °C
579 - 604 °F
Front Barrel Temperature 316 - 329 °C
601 - 624 °F
Melt Temperature 321 - 343 °C
610 - 649 °F
Mold Temperature 65.6 - 110 °C
150 - 230 °F
Drying Temperature 110 °C

@Time 14400 sec
230 °F

@Time 4.00 hour
Moisture Content <= 0.045 %
<= 0.045 %
Descriptive Properties Value Comments
Additive Impact Modifier
Lubricant
Mold Release
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Natural
Form Pellets
Processing Technique Injection Molding; Water-Heated Mold Injection Molding