SABIC Innovative Plastics LNP LUBRICOMP RFL22E PA6.6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RFL22E PA6.6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RFL22E Is a compound based on PA66 resin, containing Glass Fiber and PTFE. Added features include: Internally Lubricated, Easy Moulding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Water Absorption | 0.93 % @Time 86400 sec |
0.93 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm | 0.0050 - 0.0060 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| 4.7 % | 4.7 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 138 MPa | 20000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.50 GPa | 653 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 60.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 256 °C | 493 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 236 °C | 457 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Glow Wire Test | 675 °C | 1250 °F | IEC 60695-2-13 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1-7791 Polyamide 66, with carbon fiber, PTFE, lubricant modified, heat stabilized
- Karina E 800-10/1-A-RT PVC Compound White Color
- SABIC Innovative Plastics Xylex X7200MR PC+POLYESTER (Asia Pacific)
- SABIC Innovative Plastics NORYL N190HF PPE+HIPS (Asia Pacific)
- A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT
- Crucible Compaction Metals P/M 625 Corrosion Resistant Alloy
- Domo 1102M Polypropylene Homopolymer
- Fainplast Compounds GA 0248/4 Flexible PVC, Flame Retardant Sheathing
- BASF Capron® 8351 HS BK-102 Impact Modified Nylon 6 (Dry) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved