Samsung Cheil Industries Starex® NH-1907 HIPS, Unreinforced FR
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® NH-1907 HIPS, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 35 g/10 min @Load 10.0 kg, Temperature 220 °C |
35 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 57.9 MPa | 8390 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 79.4 MPa | 11500 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.883 J/cm @Thickness 3.17 mm |
1.65 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 96.0 °C | 205 °F | B/50; ISO R306 |
| Flammability, UL94 | V-0 @Thickness 2.50 mm |
V-0 @Thickness 0.0984 in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® IFX5420Z PC (Asia Pacific)
- LG Chemical NT-520 ABS, High Flow, Non Toxic
- Karina E 830-10/150-Y-ERYB-LMP White PVC Compound
- Lanxess Durethan® A 30 000000 Nylon 66
- SABIC Innovative Plastics LNP LUBRICOMP IBI16 PA 6/12
- Taiwan PU Corporation PPG CPU-1090C Polyurethane Casting Elastomer
- Tra-Con Tra-Bond CA20 Coil-Fix Epoxy Adhesive
- Chosun Refractories HSM-32 Heat-Setting Mortar
- Momentive Performance Materials HV 3/706 Heat Cured Rubber - High Temperature
Copyright © lookpolymers.com All Rights Reserved