SABIC Innovative Plastics LNP LUBRICOMP KL004AXC Acetal Homopolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KL004AXC Acetal Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* KL004AXC is a compound based on Acetal Homopolymer resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ASTM D792 |
| 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.230 % | 0.230 % | 50% RH, 24 hrs; ASTM D570 |
| 0.370 % | 0.370 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.020 - 0.0219 cm/cm @Time 86400 sec |
0.020 - 0.0219 in/in @Time 24.0 hour |
ISO 294 |
| 0.020 - 0.022 cm/cm @Time 86400 sec |
0.020 - 0.022 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.0219 cm/cm @Time 86400 sec |
0.020 - 0.0219 in/in @Time 24.0 hour |
ISO 294 |
| 0.020 - 0.022 cm/cm @Time 86400 sec |
0.020 - 0.022 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 9.4 % | 9.4 % | 5 mm/min; ISO 527 |
| 11.4 % | 11.4 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.55 GPa | 370 ksi | 50 mm/min; ASTM D638 |
| 2.70 GPa | 392 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| 86.0 MPa | 12500 psi | ISO 178 | |
| Flexural Modulus | 2.62 GPa | 380 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.90 GPa | 421 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.60 J/cm | 10.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.22 | 0.22 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.090 | 0.090 | ASTM D3702 Modified |
| K (wear) Factor | 24.2 x 10-8 mm³/N-M | 12.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Niche Polymer PCABSN8BK PC/ABS
- LyondellBasell Alathon® M4855 High Density Polyethylene, Injection Molding Grade
- SABIC Innovative Plastics LNP THERMOCOMP 2C004 ETFE
- Eurostar Staramide P1000IX1 PA6, Impact Modified, Injection Molded
- Arlon 56811B025 0.026" (0.660 mm) Uncured Silicone Rubber with Fiberglass Substrate
- BASF Novolen® 3300 MC Polypropylene
- Lubrizol ESTANE® 58202 Ether Based Thermoplastic Polyurethane (European Grade)
- Heraeus Clevios™ S V4 Antistatic/Conductive Polymer Coating for Screen Printing
Copyright © lookpolymers.com All Rights Reserved