- SABIC Innovative Plastics LNP LUBRICOMP KFL23LH Acetal Copolymer
SABIC Innovative Plastics LNP LUBRICOMP KFL23LH Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 20% Glass Fiber Reinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KFL23LH Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* KFL23LH is a compound based on Acetal Copolymer resin containing 15% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Low Extractable.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | ASTM D792 |
| Density | 1.58 g/cc | 0.0571 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.210 % | 0.210 % | 50% RH, 24 hrs; ASTM D570 |
| 0.340 % | 0.340 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 |
| 78.0 MPa | 11300 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 6.72 GPa | 975 ksi | 50 mm/min; ASTM D638 |
| 6.82 GPa | 989 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 107 MPa | 15500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 108 MPa | 15700 psi | ISO 178 | |
| Flexural Yield Strength | 119 MPa | 17300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.74 GPa | 833 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 5.90 GPa | 856 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.510 J/cm | 0.955 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.50 J/cm | 6.56 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 163 °C @Thickness 3.20 mm |
325 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 161 °C @Thickness 3.20 mm |
322 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1301-8306 PPS, linear, with carbon fiber, lubricant modified
- Industeel CREUSABRO® 4800 Advanced Technology in Wear Steel
- H.C. Starck Grade A Zirconium Carbide, ZrC
- Techmer ES HiFill FR® PA4/6 GF15 FR HS L 15% Glass Filled (Conditioned)
- Unipetrol PP MONSTEN® MA 611 Polypropylene Impact Copolymer
- Formosa Plastics 25% Liquid Caustic Soda Membrane Grade
- ELASTO UK Dryflex® 662850S SEBS Based Material, Semi-Filled Qualities, 85A Hardness, Black
- Eliokem Chemigum® P615D Nitrile Elastomer
- DuPont Performance Polymers Rynite® RE15022 NC010 Polyethylene Terephthalate (PET)
- Chem Polymer Chemlon 280 Nylon 6, High Impact
Copyright © lookpolymers.com All Rights Reserved