- Eurotec® Tecotek® PC40 GR20 NL PC, 20% glass fiber reinforced, natural
Eurotec® Tecotek® PC40 GR20 NL PC, 20% glass fiber reinforced, natural
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | Eurotec |
| Trade Name | Tecotek® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecotek® PC40 GR20 NL PC, 20% glass fiber reinforced, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % @Temperature 23.0 °C |
0.200 % @Temperature 73.4 °F |
50% RH; ISO 960 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 6.50 GPa | 943 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 12.0 kJ/m² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75 |
| Vicat Softening Point | 145 °C @Load 5.10 kg |
293 °F @Load 11.2 lb |
ISO 306 |
| Flammability, UL94 | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
|
| V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
||
| Glow Wire Test | 925 °C @Thickness 2.00 mm |
1700 °F @Thickness 0.0787 in |
GWIT; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Comparative Tracking Index | 175 V | 175 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 - 310 °C | 518 - 590 °F | |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | |
| Moisture Content | <= 0.10 % | <= 0.10 % | ISO 960 |
| Hold Pressure | 60.0 - 120 MPa | 8700 - 17400 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Crastin® SK615SF NC010 PBT (Unverified Data**)
- PolyOne Edgetek® SF-20CF/000 Polyphenylene Sulfide (PPS) (discontinued **)
- IPB Bicell® Cellular Polypropylene Sheet
- Mearthane Durethaneâ„¢ S DS-585DR Solid Polyurethane Elastomer
- Iran Petrochemical (PCC) HB5510 High Density Polyethylene
- Taiwan PU Corporation TPU-BH90 Hydrolysis Resistance, Blow Molding Polyether Base TPU
- Brandenburger S 5000 Ablation Material for Aeronautics and Space Aviation
- ATI Allegheny Ludlum ALFA-I™ Stainless Steel Type 406
Copyright © lookpolymers.com All Rights Reserved