SABIC Innovative Plastics LNP LUBRICOMP IN001 PA6.12
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP IN001 PA6.12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* IN001 is a compound based on Nylon 6/12 resin containing 2% Moly. Added feature of this grade is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Density | 1.084 g/cc | 0.03916 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.230 % | 0.230 % | 50% RH, 24 hrs; ASTM D570 |
| 0.310 % | 0.310 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D638 |
| 62.0 MPa | 8990 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D638 |
| 62.0 MPa | 8990 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D638 |
| 4.1 % | 4.1 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D638 |
| 4.1 % | 4.1 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.75 GPa | 399 ksi | 1 mm/min; ISO 527 |
| 2.95 GPa | 428 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.49 GPa | 361 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.330 J/cm | 0.618 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.71 J/cm | 5.08 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J @Temperature 23.0 °C |
1.48 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 89.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
49.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 96.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
53.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 174 °C @Thickness 3.20 mm |
345 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 69.0 °C @Thickness 3.20 mm |
156 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ G-2184M PVC Compound
- SABIC PP 578P Polypropylene Homopolymer for Injection Molding
- PolyOne Geon™ Vinyl Flexible R9788A Polyvinyl Chloride, Flexible (PVC, Flexible)
- Solvay Specialty Polymers Ixef® 1022 Polyarylamide (PARA) (Unverified Data**)
- Lubriplate L0750 Heat Transfer Oil Specialty Oil and Fluid
- Diamond Polymers ABS 3501E
- China Tungsten YT30 Tungsten Carbide for Cutting Tools
- Abatron AboCast 8103-11 One Part Epoxy
- Bostik 2107 General Purpose EVA Glue Stick
- Shanghai Ofluorine 904 PVDF for water UF (ultrafiltration) Membranes
Copyright © lookpolymers.com All Rights Reserved