SABIC Innovative Plastics LNP LUBRICOMP IBP34 PA6.12

Category Polymer , Thermoplastic , Nylon , Nylon 612
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP IBP34 PA6.12.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* IBP34 is a compound based on Nylon 6/12 containing 20% Glass Bead, 15% PTFE/Silicone. Added features include: Wear Resistant.
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D792
Density 1.32 g/cc
0.0477 lb/in³
ASTM D792
Moisture Absorption 0.220 %
0.220 %
50% RH, 24 hrs; ASTM D570
0.260 %
0.260 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow >= 0.020 cm/cm

@Time 86400 sec
 >= 0.020 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.020 - 0.040 cm/cm

@Time 86400 sec
 0.020 - 0.040 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.0 MPa
6380 psi
5 mm/min; ISO 527
45.0 MPa
6530 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 3.7 %
3.7 %
5 mm/min; ISO 527
3.9 %
3.9 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 3.5 %
3.5 %
5 mm/min; ISO 527
3.6 %
3.6 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 2.67 GPa
387 ksi
1 mm/min; ISO 527
2.74 GPa
397 ksi
50 mm/min; ASTM D638
Flexural Strength 73.0 MPa
10600 psi
ISO 178
76.0 MPa
11000 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.61 GPa
379 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.65 GPa
384 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.280 J/cm
0.525 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.29 J/cm
6.16 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 2.00 kJ/m²
0.952 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 18.0 kJ/m²
8.57 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 4.00 J

@Temperature 23.0 °C
 2.95 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.56
0.56
ASTM D3702 Modified
Coefficient of Friction, Static 0.59
0.59
ASTM D3702 Modified
K (wear) Factor 26.2 x 10-8 mm³/N-M
13.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 88.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 48.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
CTE, linear, Transverse to Flow 87.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 48.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 159 °C
318 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
170 °C

@Thickness 3.20 mm
 338 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
106 °C

@Thickness 3.20 mm
 223 °F

@Thickness 0.126 in
 unannealed; ASTM D648