SABIC Innovative Plastics LNP LUBRICOMP IAL12 PA6.12
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP IAL12 PA6.12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* IAL12 is a compound based on Nylon 6/12 resin containing 5% PTFE, 10% Aramid Fiber. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.210 % | 0.210 % | 50% RH, 24 hrs; ASTM D570 |
| 0.320 % | 0.320 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 63.0 MPa | 9140 psi | 5 mm/min; ISO 527 |
| 65.0 MPa | 9430 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 8.6 % | 8.6 % | Type I, 5 mm/min; ASTM D638 |
| 8.8 % | 8.8 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 8.1 % | 8.1 % | Type I, 5 mm/min; ASTM D638 |
| 8.2 % | 8.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.92 GPa | 424 ksi | 1 mm/min; ISO 527 |
| 3.16 GPa | 458 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
| Flexural Modulus | 2.63 GPa | 381 ksi | 2 mm/min; ISO 178 |
| 2.84 GPa | 412 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.92 J/cm | 9.22 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 38.0 kJ/m² | 18.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.45 | 0.45 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.40 | 0.40 | ASTM D3702 Modified |
| K (wear) Factor | 62.4 x 10-8 mm³/N-M | 31.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 85.9 µm/m-°C @Temperature -30.0 - 30.0 °C |
47.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 107 µm/m-°C @Temperature -30.0 - 30.0 °C |
59.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C | 342 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 187 °C @Thickness 3.20 mm |
369 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Rotuba 860H2 Ethyl Cellulose
- KB Alloys Tibor® 5% Ti - 0.2% B Titanium Boron Aluminum Alloy
- LG Chemical LI911 ASA
- Indium Corp. Indalloy® 4 Pure Indium Solder
- Shakespeare FN-29 Freshwater Nylon Copolymer Fishing Line, 17 lb
- Techmer ES HiFill® PA6 G/C50 A240 BK 50% Glass/Ceramic Filled
- Techmer ES Plastiblend® ABS LE WT
- Axiall 9113 Rigid PVC, Molding
- Lucent Polymers POM-500 Acetal Homopolymer, General Purpose, Injection Grade
Copyright © lookpolymers.com All Rights Reserved