SABIC Innovative Plastics LNP LUBRICOMP DX96651 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DX96651 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* DX96651 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.160 % | 0.160 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0073 cm/cm @Time 86400 sec |
0.0073 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0075 cm/cm @Time 86400 sec |
0.0075 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | ISO 527 |
| 58.0 MPa | 8410 psi | ASTM D638 | |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
| 55.0 MPa | 7980 psi | ISO 527 | |
| Tensile Modulus | 2.20 GPa | 319 ksi | 50 mm/min; ASTM D638 |
| 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| 93.0 MPa | 13500 psi | ASTM D790 | |
| Flexural Modulus | 2.48 GPa | 360 ksi | ASTM D790 |
| 2.60 GPa | 377 ksi | ISO 178 | |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 137 kJ/m² | 65.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 41.0 J | 30.2 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 128 J | 94.4 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 65.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 65.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 66.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 51 T 30 PP, 30% mineral filling
- Polimeri Europa Extir® B 3000 Expandable Polystyrene, Fast Molding (discontinued **)
- Iran Petrochemical (PCC) 2004TC37 Low Density Polyethylene
- LATI Latistat 62-06 K/10 PA6, 10% Carbon Fiber Reinforced
- Saint-Gobain CHR® SG05-05(R) Premium Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- DuPont Performance Polymers Zytel® 80G33HS1L NC010 Nylon 66 (Unverified Data**)
- Dow Saran® 469 PVDC
- Arlon 10502R010 0.010" (.254 mm) Cured/Post-Cured Unsupported Silicone Rubber
- Overview of materials for Polyvinyl Dichloride (PVDC) Coated Polyester Film
Copyright © lookpolymers.com All Rights Reserved