Polymer Resources PPX-FR6 Modified PPO, UL 94 V-0 with HDT of 300 F  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-FR6 Modified PPO, UL 94 V-0 with HDT of 300 F  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 1.0 - 3.0 g/10 min
1.0 - 3.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.3 MPa
10200 psi
ASTM D638
Tensile Strength, Yield 66.9 MPa
9700 psi
ASTM D638
Flexural Strength 98.6 MPa
14300 psi
ASTM D790
Flexural Modulus 2.34 GPa
340 ksi
ASTM D790
Izod Impact, Notched 4.27 J/cm
8.00 ft-lb/in
ASTM D256
Gardner Impact >= 22.6 J
>= 16.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 149 °C
300 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 141 °C
285 °F
ASTM D648
Flammability, UL94 V-0
V-0
1/16 in
V-0
V-0
1/8 in
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 304 °C
500 - 580 °F
Middle Barrel Temperature 271 - 310 °C
520 - 590 °F
Front Barrel Temperature 282 - 316 °C
540 - 600 °F
Melt Temperature 293 - 316 °C
560 - 600 °F
Mold Temperature 82.2 - 116 °C
180 - 240 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 3 - 4 hour
3 - 4 hour