SABIC Innovative Plastics LNP LUBRICOMP DX09407H PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DX09407H PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* DX09407H is a compound based on High Heat Polycarbonate containing proprietary fillers. Added features of this grade are: Wear Resistant, Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Moisture Absorption | 0.210 % | 0.210 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | Type I, 5 mm/min; ASTM D638 |
| 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | Type I, 5 mm/min; ASTM D638 |
| 64.0 MPa | 9280 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 68 % | 68 % | Type I, 5 mm/min; ASTM D638 |
| 76.8 % | 76.8 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| 111 % | 111 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 6.8 % | 6.8 % | Type I, 5 mm/min; ASTM D638 |
| 6.9 % | 6.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.13 GPa | 309 ksi | 1 mm/min; ISO 527 |
| 2.23 GPa | 323 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.08 GPa | 302 ksi | 2 mm/min; ISO 178 |
| 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.39 J/cm | 2.60 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 22.14 J/cm | 41.48 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 191 kJ/m² | 90.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 74.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 76.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 139 °C @Thickness 3.20 mm |
282 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- EVALCA EVAL® G110 Ethylene Vinyl Alcohol Copolymer Resin (discontinued **)
- Lubriplate 777 NO. Specialty Lubricant and Grease
- DuPont Performance Polymers Crastin® S600LF NC010 PBT
- ExxonMobil Santoprene® 9101-80E Thermoplastic Vulcanizate - Co-extrusion
- Colorite Polymers 2007UV Rigid PVC
- Arkema Group Orgalloy® LT 4060 Flexible Nylon Alloy (Conditioned)
- Caplinq LINQTAPE™ PIT1S
- AK Steel CARLITE® M-3 Grain Oriented Electrical Steel (Extended Electro-Magnetic Data)
Copyright © lookpolymers.com All Rights Reserved