| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SABIC Innovative Plastics NORYL SE1V PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE/HIPS, unfilled, FR-V1, 90 oC
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Water Absorption | 0.070 % <br>@Time 86400 sec |
0.070 % <br>@Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm <br>@Thickness 3.20 mm |
0.0050 - 0.0070 in/in <br>@Thickness 0.126 in |
SABIC Method |
| Melt Flow | 4.7 g/10 min <br>@Load 10.0 kg,<br> Temperature 250 °C |
4.7 g/10 min <br>@Load 22.0 lb,<br> Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | SABIC - Japan Method |
| Elongation at Break | 55 % | 55 % | SABIC - Japan Method |
| Flexural Strength | 85.0 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 2.45 GPa | 355 ksi | ASTM D790 |
| Izod Impact, Notched | 1.96 J/cm | 3.67 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C <br>@Temperature -30.0 - 30.0 °C |
33.3 µin/in-°F <br>@Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C <br>@Thickness 6.40 mm |
257 °F <br>@Thickness 0.252 in |
unannealed; ASTM D648 |
| Flammability, UL94 | HB <br>@Thickness 0.750 mm |
HB <br>@Thickness 0.0295 in |
UL 94 |
| V-1 <br>@Thickness 1.50 mm |
V-1 <br>@Thickness 0.0591 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 2.69 <br>@Frequency 50.0 - 60.0 Hz |
2.69 <br>@Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
Users viewing this material also viewed the following:
- Momentive Performance Materials TSE322 Heat-Curing Silicone Adhesive, Light Blue
- SABIC Innovative Plastics Valox® EH7025AG PBT+PET
- SK Chemicals SKYTHANE® S385A Polyester Based Thermoplastic Polyurethane Elastomer
- Covestro Bayblend® T 85 MN Polycarbonate/ABS Blend
- 3M 2515 Flat Back Paper Masking Tape
- 3M 4317 Foam Tape
- 3M 7215SA Screen Printable Polyester Performance Label Products with Structured Adhesive
- ExxonMobil Enable™ 35-05CH Metallocene Polyethylene Resin (European Grade)
Copyright © lookpolymers.com All Rights Reserved