SABIC Innovative Plastics LNP KONDUIT PX11311 PA 6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Konduit |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP KONDUIT PX11311 PA 6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Thermally conductive mineral and glass fiber filled PA6 Eco-FR compound
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 102 MPa | 14800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 12.5 GPa | 1810 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 164 MPa | 23800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 34.6 µm/m-°C @Temperature -30.0 - 80.0 °C |
19.2 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 | |
| 37.2 µm/m-°C @Temperature 23.0 - 80.0 °C |
20.7 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 47.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.5 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 60.4 µm/m-°C @Temperature -30.0 - 80.0 °C |
33.6 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 | |
| 73.4 µm/m-°C @Temperature 23.0 - 80.0 °C |
40.8 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Thermal Conductivity | 1.10 W/m-K | 7.63 BTU-in/hr-ft²-°F | through-plane, ø80*3mm discs; ISO 22007-2 |
| 1.30 W/m-K | 9.02 BTU-in/hr-ft²-°F | in-plane, ø80*3mm discs; ISO 22007-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 208 °C | 406 °F | Rate B/120; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.00 mm |
V-0 @Thickness 0.0394 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Comparative Tracking Index | >= 600 V | >= 600 V | UL 746A |
| 600 V | 600 V | IEC 60112 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ FR PP 301 S Polypropylene, Unspecified (PP, Unspecified)
- PolyOne Dynaflex™ G7930-1 NSFG Thermoplastic Elastomer (TPE)
- SPS Guang Zhou SAMATâ„¢ EP 5001C(f1) Flame-retarded Polypropylene
- Teknor Apex Sinpolene MBB005LE Low Density Polyethylene
- Universal Wire Works Stellite 31 (AMS 5789) Filler Metal
- Elgiloy® Co-Cr-Ni Alloy, Strip, 85% Cold Reduction, Heat Treated
- Daikin POLYFLON F-104 PTFE Fine Powder
- Carpenter BioDur™ 316LS Stainless Medical Implant Alloy, 52% Cold Worked
- Plaskolite West Optix® CA-68 General Purpose Acrylic Resin
- Techmer Lehvoss Compounds Luvotech™ J-4/35/HS NAT PA6/12 (discontinued **)
Copyright © lookpolymers.com All Rights Reserved