SABIC Innovative Plastics LNP COLORCOMP I1000 PA6.12
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Colorcomp |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP COLORCOMP I1000 PA6.12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* COLORCOMP* I1000 is an unfilled Nylon 6/12
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 100 % | 100 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 4.5 % | 4.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.39 GPa | 347 ksi | 1 mm/min; ISO 527 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 55.0 °C @Thickness 3.20 mm |
131 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Oxygen Index | 27 % | 27 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.6 @Frequency 100 Hz |
3.6 @Frequency 100 Hz |
ASTM D150 | |
| Dissipation Factor | 0.014 @Frequency 100000 Hz |
0.014 @Frequency 100000 Hz |
ASTM D150 |
| 0.020 @Frequency 100 Hz |
0.020 @Frequency 100 Hz |
ASTM D150 | |
| 0.020 @Frequency 1000 Hz |
0.020 @Frequency 1000 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 TF10 Nylon 6.6 for injection molding, 10% PTFE lubricated
- Mallard Creek Polymers ROVENE® 403 Carboxylated Acrylic Copolymer Latex
- SABIC Innovative Plastics Noryl PC180X PPE+PS
- Shin-Etsu Silicones KSG-16 Fluid
- Master Bond UV15 High Strength UV Curable Adhesive System
- UBE Z322 Polyethylene
- A. Schulman POLYTROPE™ TPP 402 Blow Molding Grade Olefinic Thermoplastic Elastomer
- ArcelorMittal Save 27-17 Electrical Steel
- Aremco Corr-Paint™ CP4040-S1 High Temperature Protective Coating, Silicone
- ChevronTexaco StarFak® PM
Copyright © lookpolymers.com All Rights Reserved