- SABIC Innovative Plastics LNP COLORCOMP G1000 PSU
SABIC Innovative Plastics LNP COLORCOMP G1000 PSU
| Category | Polymer , Thermoplastic , Polysulfone (PSU) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Colorcomp |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP COLORCOMP G1000 PSU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* COLORCOMP* G1000 is an unfilled Polysulfone resin. Added feature of this grade is: Transparent.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Moisture Absorption | 0.300 % | 0.300 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 50 - 100 % | 50 - 100 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.48 GPa | 360 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 106 MPa | 15400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.69 GPa | 390 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 56.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
31.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C @Thickness 3.20 mm |
345 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.00e+17 ohm-cm | 3.00e+17 ohm-cm | ASTM D257 |
| Dissipation Factor | 0.00070 @Frequency 50.0 - 60.0 Hz |
0.00070 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| 0.0010 @Frequency 1000 Hz |
0.0010 @Frequency 1000 Hz |
ASTM D150 | |
| 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® 1509 Emulsion Styrene-Butadiene Rubber
- Orion Engineered Carbons ECORAX® S 247 Carbon Black
- Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F)
- Polyplastics Duranex® 3105 Polybutylene Terephthalate (PBT), Standard, 15% GF filled
- Polyram PlusTek PA823M6 Nylon 6.6 for Injection Molding, 30% Minerals Reinforced, Impact Modified
- A. Schulman POLYBATCH™ Red 5400 Concentrate Based In Polyethylene
- Lubrizol ESTANE® 58144 Ether Based Thermoplastic Polyurethane (European Grade)
- Daikin DAI-EL G-704 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
- CMT Materials HYTAC® C Castable Syntactic Tooling
- 3M Scotchcal™ ElectroCut™ 7125-131 Graphic Film
Copyright © lookpolymers.com All Rights Reserved