SABIC Innovative Plastics LNP COLORCOMP D1000P PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Colorcomp |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP COLORCOMP D1000P PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* COLORCOMP* D1000P is an unfilled Polycarbonate. Added feature of this grade is: Exceptional Processing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.0065 cm/cm @Time 86400 sec |
0.0065 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm @Time 86400 sec |
0.0075 in/in @Time 24.0 hour |
ISO 294 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | ASTM D638 |
| 59.0 MPa | 8560 psi | ISO 527 | |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | ASTM D638 |
| 64.0 MPa | 9280 psi | ISO 527 | |
| Elongation at Break | 78.7 % | 78.7 % | ASTM D638 |
| 87 % | 87 % | ISO 527 | |
| Elongation at Yield | 5.3 % | 5.3 % | ASTM D638 |
| 5.6 % | 5.6 % | ISO 527 | |
| Tensile Modulus | 2.06 GPa | 299 ksi | 50 mm/min; ASTM D638 |
| 2.21 GPa | 321 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 81.0 MPa | 11700 psi | ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| 2.75 GPa | 399 ksi | ASTM D790 | |
| Izod Impact, Notched | 5.44 J/cm | 10.2 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPH4704 PPC (Asia Pacific)
- Pau Tai UNISTAB OTM-17 Organo Tin Stabilizer
- H.C. Starck Amperit® 413.6 Gas Atomized (NiCoCrAlY)
- Saint-Gobain CHR® T903 TRIFOIL™ PTFE/Aluminum Foil Backing Silicone Adhesive Pressure Sensitive Tape
- Hexcel® HexWeb® CR-PAA™ 1/4-5056-0.001 Phosphoric Acid Anodized Aluminum Honeycomb
- DuPont™ Bynel® 21E787 Anhydride Modified Ethylene Acrylate
- Fainplast Compounds CL 80 Flexible PVC, Sheathing
- ATI Allegheny Ludlum Grade 23 (6-4 ELI) Titanium (UNS R56401)
- Bulk Molding Compounds BMC 501 Mineral Filled, Glass Fiber Reinforced Compound
Copyright © lookpolymers.com All Rights Reserved