- SABIC Innovative Plastics GELOY CR7501 ASA (Europe-Africa-Middle East)
SABIC Innovative Plastics GELOY CR7501 ASA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ASA Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | GELOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics GELOY CR7501 ASA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High heat injection moulding grade, blend of ASA/AMSAN. It can be positioned for outside parts in various markets. Various colours.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.55 % | 0.55 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 9.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
9.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 |
| 49.0 MPa | 7110 psi | 50 mm/min; ISO 527 | |
| Elongation at Yield | 2.8 % | 2.8 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.38 GPa | 345 ksi | 1 mm/min; ISO 527 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Taber Abrasion, mg/1000 Cycles | 155 | 155 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.210 W/m-K | 1.46 BTU-in/hr-ft²-°F | ISO 8302 |
| Vicat Softening Point | 102 °C | 216 °F | Rate B/50; ISO 306 |
| 106 °C | 223 °F | Rate B/120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- PTS Tristar® PC-10R-(V22) 22 MFI UV Stabilized Polycarbonate With Release
- Karina TR-551D48/1 Black PVC Compound
- SK Chemicals SKYTHANE® 310 Hotmelt Grade UB Polyurethane
- Tra-Con Tra-Bond F125 Fast Gel Clear Epoxy Adhesive
- Entec Hypro™ PP-CP35/2 Impact Copolymer, 35 Melt Flow
- DuPont Performance Polymers Zytel® FE3734 NC010 Nylon 612 (Unverified Data**)
- Asahi Glass Lumiflon LF-810 Solvent Soluble Fluoropolymer
- Arlon AD320 Glass, PTFE and Micro-Dispersed Ceramic
- IRPC Polimaxx Pentfoam 526W Expandable Polystyrene
Copyright © lookpolymers.com All Rights Reserved