SABIC Innovative Plastics Cycoloy® NX07353 PC+ABS (Asia Pacific)

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Cycoloy®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Cycoloy® NX07353 PC+ABS (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Cycoloy* C7230P resin is a mineral filled, flame retardant PC/ABS. Good stiffness combined with balanced flow and impact performance, makes it a good candidate for various applications.

Physical Properties	Metric	English	Comments
Specific Gravity	1.30 g/cc	1.30 g/cc	ASTM D792
Density	1.30 g/cc	0.0470 lb/in³	ISO 1183
Moisture Absorption	0.0400 %	0.0400 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	0.090 %	0.090 %	ISO 62
Linear Mold Shrinkage, Flow	0.0025 - 0.0035 cm/cm @Thickness 3.20 mm	0.0025 - 0.0035 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	13 g/10 min @Load 2.16 kg, Temperature 260 °C	13 g/10 min @Load 4.76 lb, Temperature 500 °F	ASTM D1238
Melt Index of Compound	9.0 g/10 min @Load 2.16 kg, Temperature 260 °C	9.0 g/10 min @Load 4.76 lb, Temperature 500 °F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	35.0 MPa	5080 psi	50 mm/min; ISO 527
	43.0 MPa	6240 psi	Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield	55.0 MPa	7980 psi	Type I, 50 mm/min; ASTM D638
	55.0 MPa	7980 psi	50 mm/min; ISO 527
Elongation at Break	30 %	30 %	50 mm/min; ISO 527
Elongation at Yield	3.8 %	3.8 %	50 mm/min; ISO 527
	4.0 %	4.0 %	Type I, 50 mm/min; ASTM D638
Tensile Modulus	5.19 GPa	753 ksi	5 mm/min; ASTM D638
	5.58 GPa	809 ksi	1 mm/min; ISO 527
Flexural Yield Strength	95.0 MPa	13800 psi	1.3 mm/min, 50 mm span; ASTM D790
	99.0 MPa	14400 psi	2 mm/min; ISO 178
Flexural Modulus	4.53 GPa	657 ksi	1.3 mm/min, 50 mm span; ASTM D790
	4.58 GPa	664 ksi	2 mm/min; ISO 178
Izod Impact, Notched	0.650 J/cm	1.22 ft-lb/in	ASTM D256
	0.480 J/cm @Temperature -30.0 °C	0.899 ft-lb/in @Temperature -22.0 °F	ASTM D256
Izod Impact, Notched (ISO)	5.00 kJ/m²	2.38 ft-lb/in²	80104; ISO 180/1A
	5.00 kJ/m² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²	Edgew 80104 sp=62mm; ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	42.0 µm/m-°C @Temperature -40.0 - 40.0 °C	23.3 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	42.0 µm/m-°C @Temperature -40.0 - 40.0 °C	23.3 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
CTE, linear, Transverse to Flow	49.0 µm/m-°C @Temperature -40.0 - 40.0 °C	27.2 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	59.0 µm/m-°C @Temperature -40.0 - 40.0 °C	32.8 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	89.0 °C	192 °F	Flatw 80104 sp=64mm; ISO 75/Af
	88.0 °C @Thickness 3.20 mm	190 °F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	107 °C	225 °F	Rate B/50; ISO 306
	108 °C	226 °F	Rate B/50; ASTM D1525
	110 °C	230 °F	Rate B/120; ISO 306
Flammability, UL94	V-0 @Thickness 1.20 mm	V-0 @Thickness 0.0472 in	UL 94
	5VB @Thickness 2.00 mm	5VB @Thickness 0.0787 in	UL 94