Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CY200FC PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High flow PC+ABS material designed for local Pacific Automotive applications
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D792
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Moisture Absorption 0.0200 %
0.0200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.20 %
0.20 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0090 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0090 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 18 g/10 min

@Load 5.00 kg,
Temperature 260 °C
18 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 17 g/10 min

@Load 5.00 kg,
Temperature 260 °C
17 g/10 min

@Load 11.0 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
Type I, 50 mm/min; ASTM D638
53.0 MPa
7690 psi
50 mm/min; ISO 527
Tensile Strength, Yield 53.0 MPa
7690 psi
Type I, 50 mm/min; ASTM D638
53.0 MPa
7690 psi
50 mm/min; ISO 527
Elongation at Break 100 %
100 %
Type I, 50 mm/min; ASTM D638
100 %
100 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
5.0 %
5.0 %
50 mm/min; ISO 527
Tensile Modulus 2.25 GPa
326 ksi
1 mm/min; ISO 527
2.30 GPa
334 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 80.0 MPa
11600 psi
2 mm/min; ISO 178
82.0 MPa
11900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.20 GPa
319 ksi
2 mm/min; ISO 178
2.25 GPa
326 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 4.70 J/cm
8.81 ft-lb/in
ASTM D256
3.70 J/cm

@Temperature -30.0 °C
6.93 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
80*10*3; ISO 180/1A
25.0 kJ/m²

@Temperature -30.0 °C
11.9 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 5.00 J/cm²
23.8 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
2.50 J/cm²

@Temperature -30.0 °C
11.9 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 60.0 J

@Temperature 23.0 °C
44.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 102 °C
216 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
100 °C

@Thickness 3.20 mm
212 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 122 °C
252 °F
Rate B/50; ASTM D1525
122 °C
252 °F
Rate B/50; ISO 306
123 °C
253 °F
Rate B/120; ISO 306