SABIC Innovative Plastics Cycolac® X11 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® X11 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive: High heat resistance. Excellent flow/impact balance. UL94 HB rated. High gloss.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Viscosity | 225000 cP | 225000 cP | Melt Viscosity, 260°C, 1000 sec-1; ASTM D3825 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 1.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.06 GPa | 299 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 68.0 MPa | 9860 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.13 GPa | 309 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 3.20 J/cm | 5.99 ft-lb/in | ASTM D256 |
| 0.850 J/cm @Temperature -40.0 °C |
1.59 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 91.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
51.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 90.0 °C @Thickness 6.40 mm |
194 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | UL 746A |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
Users viewing this material also viewed the following:
- ExxonMobil Escorene® LL-3001 LLDPE/Hexene Premium Film Resin, Tough, 0.6 mil Film (discontinued **)
- MarkeTech Zirconium Oxide Ceramic, Zirconia MgO Stabilized
- Fujipoly Industries FLAT-5TV-8-1.0 silicone rubber fusible tape
- Kolon KOLEFIN® KO133MT30 M/F Reinforced Polypropylene
- SABIC Innovative Plastics ULTEM 2310EPR PEI
- Samsung Cheil Industries Starex® SD-0150AT ABS, Unreinforced
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR Laminar Filler
- Total PPH 3925WZ Polypropylene, Injection Molding Grade
- ExxonMobil Escorene™ UL 00728CC Ethylene Vinyl Acetate Copolymer (European Grade)
- Arlon 920-05B##-P1 0.020" (0.508 mm) Cured Self-fusing Silicone Tape
Copyright © lookpolymers.com All Rights Reserved