SABIC Innovative Plastics LNP Thermocomp UC008S PPA (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp UC008S PPA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* UC008S is a compound based on Polyphthalamide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.40 % @Time 86400 sec |
0.40 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 232 MPa | 33600 psi | ISO 527 |
| 261 MPa | 37900 psi | ASTM D 638 | |
| Elongation at Break | 1.0 % | 1.0 % | ASTM D 638 |
| 1.3 % | 1.3 % | ISO 527 | |
| Tensile Modulus | 33.78 GPa | 4899 ksi | 50 mm/min; ASTM D 638 |
| 35.53 GPa | 5153 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 425 MPa | 61600 psi | ISO 178 |
| 441 MPa | 64000 psi | ASTM D 790 | |
| Flexural Modulus | 26.59 GPa | 3857 ksi | ISO 178 |
| 26.82 GPa | 3890 ksi | ASTM D 790 | |
| Izod Impact, Notched | 0.580 J/cm @Temperature 23.0 °C |
1.09 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.20 J/cm @Temperature 23.0 °C |
5.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | >= 250 °C | >= 482 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| >= 248 °C @Thickness 3.20 mm |
>= 478 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D 257 |
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 50/CF/15/TF/15/SI/2/BK-HB Polycarbonate, with carbon fiber, PTFE, lubricant modified
- International Mold Steel Premium H13 Hot Work Die and Mold Steel
- SABIC Innovative Plastics LNP THERMOCOMP RF008ESZ PA 66
- Master Bond EP51 Fast Curing High Bond Strength Epoxy Adhesive
- Polyram PlusTek PA108 Nylon6/6.6 Alloy for Injection Molding
- Goodfellow Nickel 80/Molybdenum 20 Alloy
- Diamond Polymers ABS 3502
- DuPont Performance Polymers VESPEL TP-8054 Polyimide
- Armstrong A-4/A Epoxy Adhesive
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR Laminar Filler
Copyright © lookpolymers.com All Rights Reserved