POLYMER SEARCH

SABIC Innovative Plastics Cycolac® INP563 ABS+SAN

Category	Polymer , Thermoplastic , ABS Polymer
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Cycolac®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Cycolac® INP563 ABS+SAN.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

SABIC INP563 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pelletized and dry blend concentrate; provides a base resin with less heat history than pellets; suitable for direct weather exposure; can be used in all SAN applications where a fine particle size is desired.

Physical Properties	Metric	English	Comments
Specific Gravity	1.08 g/cc	1.08 g/cc	ASTM D792
Density	1.08 g/cc	0.0390 lb/in³	ISO 1183
Melt Flow	19.5 g/10 min @Load 3.80 kg, Temperature 230 °C	19.5 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D1238
	47 g/10 min @Load 10.0 kg, Temperature 220 °C	47 g/10 min @Load 22.0 lb, Temperature 428 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	123	123	ASTM D785
Tensile Strength at Break	69.0 MPa	10000 psi	Type I, 5 mm/min; ASTM D638
	74.0 MPa	10700 psi	50 mm/min; ISO 527
Tensile Strength, Yield	69.0 MPa	10000 psi	Type I, 5 mm/min; ASTM D638
	74.0 MPa	10700 psi	50 mm/min; ISO 527
Elongation at Break	2.0 %	2.0 %	50 mm/min; ISO 527
	2.4 %	2.4 %	Type I, 5 mm/min; ASTM D638
Elongation at Yield	2.0 %	2.0 %	50 mm/min; ISO 527
	2.4 %	2.4 %	Type I, 5 mm/min; ASTM D638
Tensile Modulus	3.86 GPa	560 ksi	5 mm/min; ASTM D638
	3.97 GPa	576 ksi	1 mm/min; ISO 527
Flexural Yield Strength	46.0 MPa	6670 psi	2 mm/min; ISO 178
	93.0 MPa	13500 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	3.46 GPa	502 ksi	2 mm/min; ISO 178
	3.77 GPa	547 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	0.180 J/cm	0.337 ft-lb/in	ASTM D256
	0.220 J/cm @Temperature -30.0 °C	0.412 ft-lb/in @Temperature -22.0 °F	ASTM D256
Izod Impact, Notched (ISO)	2.00 kJ/m²	0.952 ft-lb/in²	80104; ISO 180/1A
	2.00 kJ/m² @Temperature -30.0 °C	0.952 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
Charpy Impact, Notched	0.100 J/cm²	0.476 ft-lb/in²	ISO 179/2C

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C @Thickness 3.20 mm	203 °F @Thickness 0.126 in	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	85.0 °C	185 °F	Flatw 80104 sp=64mm; ISO 75/Af
	82.0 °C @Thickness 3.20 mm	180 °F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	102 °C	216 °F	Rate B/50; ISO 306
	104 °C	219 °F	Rate B/120; ISO 306