- Polycarbonate, Unreinforced, Flame Retardant
- Ravago Manufacturing Americas Hylex® P1310FRMA Polycarbonate
Ravago Manufacturing Americas Hylex® P1310FRMA Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant , Polycarbonate, UV Stabilized |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylex® P1310FRMA Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate, General Purpose, Flame Retardant, UV StabilizedInformation provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Water Absorption | 0.14 % @Time 7200 sec |
0.14 % @Time 2.00 hour |
Immersed; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm @Thickness 3.17 mm |
0.0050 - 0.0070 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Tensile Strength at Break | 66.0 MPa | 9570 psi | ASTM D638 |
| Elongation at Break | 120 % | 120 % | ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Vicat Softening Point | 152 °C | 305 °F | ASTM D1525 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| V-0 - 5VA @Thickness 3.00 mm |
V-0 - 5VA @Thickness 0.118 in |
Users viewing this material also viewed the following:
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 8.0 PHR DBPH-50
- Lucas-Milhaupt HANDY HI-TEMP 548® Carbide Brazing Alloy
- LG Chemical XR407E ABS, Heat Resistance
- SYNTHOS Kralex® 1706 Styrene Butadiene Rubber
- Silberline Sparkle Silver® Premier 572
- Covestro Makrolon® GF8001* Polycarbonate, 20% Glass Filled
- BASF Caprolactam Liquid
- SABIC Innovative Plastics LNP THERMOTUF OF006I PPS - Linear
Copyright © lookpolymers.com All Rights Reserved