LG Chemical LUPOY GN2101F PC+GF10%, Halogen Free, Flame Retardant, Heat Resistance

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LG Chemical LUPOY GN2101F PC+GF10%, Halogen Free, Flame Retardant, Heat Resistance.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: Injection Molding, PC+GF10%, Halogen Free Flame Retardant, Heat ResistanceApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 65997-17-3Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
<br>@Thickness 3.20 mm
 0.0020 - 0.0040 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 8.0 g/10 min
<br>@Load 1.20 kg,<br> Temperature 300 °C
 8.0 g/10 min
<br>@Load 2.65 lb,<br> Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 124
124
ASTM D785
Tensile Strength, Yield 76.5 MPa
<br>@Thickness 3.20 mm
 11100 psi
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 7.0 %
<br>@Thickness 3.20 mm
 7.0 %
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 123 MPa
<br>@Thickness 3.20 mm
 17800 psi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 3.53 GPa
<br>@Thickness 3.20 mm
 512 ksi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched >= 0.785 J/cm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 >= 1.47 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 138 °C
<br>@Thickness 6.40 mm
 >= 280 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 120 °C
<br>@Thickness <=1.50 mm
 248 °F
<br>@Thickness <=0.0591 in
120 °C
<br>@Thickness <=3.00 mm
 248 °F
<br>@Thickness <=0.118 in
UL RTI, Mechanical with Impact 90.0 °C
<br>@Thickness >=1.50 mm
 194 °F
<br>@Thickness >=0.0591 in
90.0 °C
<br>@Thickness >=3.00 mm
 194 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical without Impact 105 °C
<br>@Thickness >=1.50 mm
 221 °F
<br>@Thickness >=0.0591 in
105 °C
<br>@Thickness >=3.00 mm
 221 °F
<br>@Thickness >=0.118 in
Flammability, UL94 V-0
<br>@Thickness >=1.50 mm
 V-0
<br>@Thickness >=0.0591 in
V-0
<br>@Thickness >=3.00 mm
 V-0
<br>@Thickness >=0.118 in
5VB
<br>@Thickness >=3.00 mm
 5VB
<br>@Thickness >=0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 270 - 300 °C
518 - 572 °F
Injection Molding
Middle Barrel Temperature 280 - 310 °C
536 - 590 °F
Injection Molding
Front Barrel Temperature 290 - 330 °C
554 - 626 °F
Injection Molding
Nozzle Temperature 290 - 330 °C
554 - 626 °F
Injection Molding
Melt Temperature 300 - 340 °C
572 - 644 °F
Injection Molding
Mold Temperature 90.0 - 120 °C
194 - 248 °F
Injection Molding
Drying Temperature 100 - 120 °C
212 - 248 °F
Injection Molding
Dry Time 3.00 - 5.00 hour
3.00 - 5.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding