Quantum Nylon 6/6 MoS2 Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, MoS2 Filled |
| Manufacturer | Quantum Advanced Engineering Plastics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quantum Nylon 6/6 MoS2 Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Quantum Advanced Engineering Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | ASTM D570 |
| Water Absorption at Saturation | 8.5 % | 8.5 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength | 82.7 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Tensile Modulus | 3.28 GPa | 475 ksi | ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 3.31 GPa | 480 ksi | ASTM D790 |
| Compressive Strength | 110 MPa | 16000 psi | ASTM D695 |
| Compressive Modulus | 2.90 GPa | 420 ksi | ASTM D695 |
| Shear Strength | 72.4 MPa | 10500 psi | ASTM D732 |
| Izod Impact, Notched | 0.374 J/cm | 0.700 ft-lb/in | ASTM D256 |
| Coefficient of Friction | 0.25 | 0.25 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 72.0 - 79.2 µm/m-°C | 40.0 - 44.0 µin/in-°F | ASTM D696 |
| Thermal Conductivity | 0.245 W/m-K | 1.70 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 260 °C | 500 °F | ASTM D3417 |
| Maximum Service Temperature, Air | 104 °C | 220 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 470 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 13.8 kV/mm | 350 kV/in | ASTM D149 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FDA Compliance | no |
Users viewing this material also viewed the following:
- Covestro Bayblend® 2773 Polycarbonate + ABS Blend, Automotive (discontinued **)
- Indium Corp. Standard ITO Indium Tin Oxide
- Karina E 605D06/476-AT Blue PVC Compound
- Momentive Performance Materials RTV6703 One-Component, Modified Alkoxy Adhesive Sealant, Black
- Shakespeare FN-29 Freshwater Nylon Copolymer Fishing Line, 15 lb
- Shakespeare WonderThread® SN-40 ultra soft TEX# 8 Nylon Industrial Sewing Thread
- ExxonMobil Mobil Clean 10W-40 5000
- Arkema Group Pebax® 7033 SA 01 MED Polyether Block Amide (PEBA)
- 3M Scotchcal™ 50-483 Graphic Film
- Loctite® PRISM® 401 Instant Adhesive
Copyright © lookpolymers.com All Rights Reserved