Qualchem Danamid AFGF-50 Polyamide 66, 50% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Qualchem Zrt. |
| Trade Name | Danamid |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Qualchem Danamid AFGF-50 Polyamide 66, 50% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Reinforced with glass fiberInformation provided by Qualchem Zrt.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | DIN 53479 |
| Filler Content | 48 - 52 % | 48 - 52 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | >= 180 MPa | >= 26100 psi | 50 mm/min; ISO 527-1,2 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1,2 |
| Tensile Modulus | >= 9.50 GPa | >= 1380 ksi | ISO 527-1,2 |
| Charpy Impact Unnotched | >= 3.00 J/cm² @Temperature 23.0 °C |
>= 14.3 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Charpy Impact, Notched | >= 0.800 J/cm² @Temperature -20.0 °C |
>= 3.81 ft-lb/in² @Temperature -4.00 °F |
DIN 53453 |
| >= 1.00 J/cm² @Temperature 23.0 °C |
>= 4.76 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 4.00 mm |
HB @Thickness 0.157 in |
MSZ 10383 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | 1.2 - 1.6 % | 1.2 - 1.6 % | DIN 53714 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ GM-3285 PVC Compound
- KB Alloys 3.5% Strontium Aluminum Alloy
- Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet
- LyondellBasell Hifaxâ„¢ RTA3263EUV/1 Thermoplastic Polyolefin Elastomer
- SABIC Innovative Plastics LNP STAT-KON RFD04 PA 66
- Styrolution PS 1621 GPPS
- Westlake EMAC® SP2260 24% Ethylene-Methyl Acrylate Copolymer
- Westlake Epolene® C-15P Coating Grade - Branched Medium Molecular Weight Polyethylene Polymer
- SABIC Innovative Plastics LNP STAT-KON MFD02 PP (Asia Pacific)
- DuPont Performance Polymers Hypalon® 45 Chlorosulfonated Polyethylene Rubber, General Description (discontinu
Copyright © lookpolymers.com All Rights Reserved