- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- LTL Color Compounds ColorFast® FRA205 ABS
LTL Color Compounds ColorFast® FRA205 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® FRA205 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame-retarded V0, high gloss ABS with superior UV stabilityAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | 0.125; ASTM D955 |
| Melt Flow | 11 g/10 min @Load 3.80 kg, Temperature 230 °C |
11 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D785 |
| Tensile Strength, Yield | 38.6 MPa | 5600 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 12 % | 12 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 57.9 MPa | 8400 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm @Temperature 22.8 °C |
4.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 72.8 °C | 163 °F | Unannealed (0.250"); ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 171 - 182 °C | 340 - 360 °F | |
| Middle Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Front Barrel Temperature | 210 - 221 °C | 410 - 430 °F | |
| Nozzle Temperature | 193 - 221 °C | 380 - 430 °F | |
| Melt Temperature | 193 - 232 °C | 380 - 450 °F | |
| Mold Temperature | 71.1 - 82.2 °C | 160 - 180 °F | |
| Drying Temperature | 71.1 - 82.2 °C | 160 - 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | nominal; maximum drying time of 8 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 50 - 70 % | 50 - 70 % | |
| Vent Depth | 0.00381 - 0.00508 cm | 0.00150 - 0.00200 in | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm |
Users viewing this material also viewed the following:
- Nye Lubricants 230 (SO) Synthetic Oil
- PPT LSF180 Low Sintering Temperature Ferrite Powder
- Overview of materials for Nylon, Amorphous Transparent Alloy
- Karina 85/277-D-AT-IS Clear PVC Compound
- Samsung Cheil Industries Infino® FD-1112 PC, FR
- Techmer ES Luriblend® ABS TL2
- Unifrax Fiberfrax® HSA (OF) Ceramic Fiber Paper
- ChevronTexaco Wheel End Grease
- DuPont Performance Polymers Zytel® 101L BKB080 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved