Polyram RamTal PM1509 Acetal, Low Friction
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTal PM1509 Acetal, Low Friction.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyacetal copolymer for decreased friction and improved wear resistance for injection molding applications.Information provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | DIN 53479 |
| Water Absorption | 0.22 % | 0.22 % | DIN 53495 |
| Linear Mold Shrinkage | 0.020 - 0.025 cm/cm | 0.020 - 0.025 in/in | |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 80 | 80 | ASTM-D785 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ASTM-D638 |
| Elongation at Break | 50 % | 50 % | ASTM-D638 |
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM-D790 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.750 J/cm @Temperature 23.0 °C |
1.41 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz |
3.8 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 BT LS PA66, basic type
- Overview of materials for Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled
- FloMet Permalloy® 4-79 Moly Soft Magnetic Alloy
- Shandong Dongyue Shenzhou New Material Co Tetrafluoroethane Β-sultone
- SABIC Innovative Plastics NORYL FXN4020H PPE+HIPS
- UBE F022 Polyethylene
- 3M Scotchcal™ 50-84 Graphic Film
- Carpenter Custom 455® Stainless Steel, Condition H1000 (Age Hardened 538°C (1000°F))
- Dielectric Polymers NT-5002 Protective Film (discontinued **)
Copyright © lookpolymers.com All Rights Reserved