- HOME
- POLYMER SEARCH
- Thermoplastic
- Polypropylene (PP)
- Polypropylene, Mineral Reinforced
- Polyram RamOfin PPC371B73 Polypropylene, 73% Mineral Filled
Polyram RamOfin PPC371B73 Polypropylene, 73% Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamOfin PPC371B73 Polypropylene, 73% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
73% mineral filled polypropylene for heavy density injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.20 g/cc | 0.0795 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | ASTM-D638 |
| Elongation at Break | 15 % | 15 % | ASTM-D638 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ASTM-D790 |
| Flexural Strength | 25.0 MPa | 3630 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.800 J/cm @Temperature 23.0 °C |
1.50 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
Users viewing this material also viewed the following:
- Piezo Kinetics 802 Lead Zirconate Titanate Piezoelectric
- Kazanorgsintez Ethyleneglycol
- Hyosung Topilene F501 PP
- Gouda Vuurvast CURON 130 HRC Dense Refractory Castable
- Loctite® Gasket Eliminator® 509 Flange Sealant
- DSM Akulon® K224-G8 PA6-GF40
- LATI LARPEEK 50 G/20 20% Glass Reinforced Polyetheretherketone (PEEK) (discontinued **)
- Solvay Specialty Polymers Primef® 4002 40% GF PPS, High Fluidity Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved