Polyram RamLloy PA917G6 PP/NYLON 66 alloy, 30% Glass Fiber

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Polypropylene (PP)
Manufacturer	Polyram
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polyram RamLloy PA917G6 PP/NYLON 66 alloy, 30% Glass Fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

30% glass fiber reinforced PA66/PP alloy with reduced water absorption, dimensional stability and UV stabilized for injection molding applicationsInformation provided by Polyram Ram On Ind.

Physical Properties	Metric	English	Comments
Density	1.31 g/cc	0.0473 lb/in³	DIN 53479
Water Absorption	3.0 %	3.0 %	DIN 53495
Moisture Absorption at Equilibrium	1.2 %	1.2 %	DIN 53714
Linear Mold Shrinkage	0.0030 - 0.0050 cm/cm	0.0030 - 0.0050 in/in

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	121	121	ASTM-D785
Tensile Strength, Yield	145 MPa	21000 psi	ASTM-D638
Elongation at Break	3.0 %	3.0 %	ASTM-D638
Flexural Strength	195 MPa	28300 psi	ASTM-D790
Flexural Modulus	5.70 GPa	827 ksi	ASTM-D790
Izod Impact, Notched	1.30 J/cm @Temperature 23.0 °C	2.44 ft-lb/in @Temperature 73.4 °F	ASTM-D256

Thermal Properties	Metric	English	Comments
Melting Point	256 °C	493 °F
Maximum Service Temperature, Air	80.0 °C	176 °F	Continuous Use
	150 °C	302 °F	Short peaks operation
Flammability, UL94	HB @Thickness 3.00 mm	HB @Thickness 0.118 in