- Lehmann & Voss LUVOCOM® 1-8181 Polyamide 66, with carbon fiber, toughness-modified
Lehmann & Voss LUVOCOM® 1-8181 Polyamide 66, with carbon fiber, toughness-modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1-8181 Polyamide 66, with carbon fiber, toughness-modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; impact resistance.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Low warpage.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 110 MPa | 16000 psi | |
| Elongation at Yield | 5.2 % | 5.2 % | |
| 6.8 % | 6.8 % | flexural | |
| Modulus of Elasticity | 8.00 GPa | 1160 ksi | |
| Flexural Strength | 160 MPa | 23200 psi | |
| Flexural Modulus | 6.00 GPa | 870 ksi | |
| Charpy Impact Unnotched | 6.30 J/cm² | 30.0 ft-lb/in² | edgewise; ISO 179 1eU |
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| 150 °C | 302 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+8 ohm | >= 1.00e+8 ohm | |
| Insulation Resistance | >= 1.00e+8 ohm | >= 1.00e+8 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Nilit RECONYL B GV30 Recycled nylon 6 for injection molding, 30% glass fiber reinforced
- PolyOne Geon™ Vinyl Flexible R277AM Polyvinyl Chloride + NBR (PVC+NBR)
- LG Chemical LUPOY GN1006FL PC, Halogen Free, Flame Retardant, Transparency
- H.C. Starck Grade K2 Crystalline Boron
- Ineos N00G-01 Polypropylene Impact Copolymer
- Techmer ES HiFill® PBT GF30 BK 30% Glass Filled
- DSM Akulon® K222-KGV4 /A PA6-GF20 FR(30)
- CLAL-MSX DECLAFOR® 1015 TD1 Wire quenched/Cold Rolled Copper Alloy
- Parker Chomerics CHO-BOND 1075 Silicone RTV Adhesive/Sealant
Copyright © lookpolymers.com All Rights Reserved