- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- GRECO ISOPAK 547 ABS Resin
GRECO ISOPAK 547 ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | GRECO |
| Trade Name | ISOPAK |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | GRECO ISOPAK 547 ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Impact GradeInformation provided by Greater Eastern Resins Industrial Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Water Absorption | 0.30 % @Temperature 23.0 °C, Time 86400 sec |
0.30 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Melt Flow | 0.50 - 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.50 - 1.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength | 47.1 MPa | 6830 psi | ASTM D638 |
| Elongation at Break | 28 % | 28 % | ASTM D412 |
| Flexural Yield Strength | 73.5 MPa | 10700 psi | ASTM D790 |
| Flexural Modulus | 2.35 GPa | 341 ksi | ASTM D790 |
| Izod Impact, Notched | 2.75 J/cm | 5.14 ft-lb/in | ASTM D256 A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | ASTM D648 |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL-746B |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Wire Ignition, HWI | 16 sec | 16 sec | .062" and above; UL-746A |
| High Amp Arc Ignition, HAI | 200 arcs | 200 arcs | .062" and above; UL-746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 mm/min | 0.000 in/min | .062" and above; UL-746A |
Users viewing this material also viewed the following:
- Polimeros Mexicanos Rotolene® Industrial Black Linear Medium Density Polyethylene
- 3M Dyneon™ PFA 6503 A EPC Perfluoroalkoxy Fluorothermoplastic (discontinued **)
- Latrobe Lescalloy® 4340 VAC-ARC ; 3.5" round High Strength Alloy Steel
- Shandong Rike Chemical HELIâ„¢ HG-400 PVC Processing Aid Series (PA)
- Schott N-LAF7 Glass
- A. Schulman SCHULAMID® 6 GF15H 15% Glass Bead Reinforced, Heat Stabilized Nylon 6
- Arlon 55572GA028 0.028" Cured Silicone Rubber with Fiberglass Substrate
- BASF Ultramid® B3EG7 35% Glass Filled PA6 (Conditioned)
- 3M Scotch® 3311 Foil Tape
- Fainplast Compounds PM 82/FR Flexible PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved