Techmer ES HiFill® PBT 0158 S
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PBT 0158 S.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: MetalInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ASTM D792 |
| Water Absorption | 0.80 % @Time 86400 sec |
0.80 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm @Thickness 3.17 mm |
0.016 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Yield | 48.3 MPa | 7000 psi | ASTM D638 |
| Elongation at Break | 16 % | 16 % | ASTM D638 |
| Flexural Strength | 68.9 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 3.03 GPa | 440 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.17 mm |
0.800 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 126 µm/m-°C | 70.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.4 °C | 130 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.00e+15 ohm-cm | 3.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.1 kV/mm | 410 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PE 4115N (16401) Linear Low Density Polyethylene
- Parker Chomerics Tecknit Teckfip™ FIP-E Formed in Place Conductive Elastomer
- Lehmann & Voss LUVOCOM® 50-1396 Polycarbonate, with carbon fiber, glass fiber and PTFE, electrically conducting
- ExxonMobil 220 Mobil DTE PM Ashless
- Elektro-Isola G-Etronax PM 953 Polyester, Glass Mat, Off White, Sheets
- ExxonMobil Bicor™ 20MB400 OPP Film
- ExxonMobil LD 071.LQ Blown Film Resin
- Ashley Polymers Ashlene® 990L-30G Nylon 610, 30% Glass Reinforced
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 302, 30% Cold Rolled (UNS S30200)
- Momentive Performance Materials RTV630 Blue General Purpose Potting/Encapsulating Compound
Copyright © lookpolymers.com All Rights Reserved