Polyram PlusTek RA304G6 Nylon 6.6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RA304G6 Nylon 6.6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass fiber reinforced, heat stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | DIN 53479 |
| Water Absorption | 5.6 % | 5.6 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM-D785 |
| Tensile Strength, Yield | 170 MPa | 24700 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Flexural Strength | 280 MPa | 40600 psi | ASTM D790 |
| Flexural Modulus | 7.80 GPa | 1130 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.00 J/cm @Temperature 23.0 °C |
1.87 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous Use |
| >= 200 °C | >= 392 °F | Short peaks operation | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | DIN 53482 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Pinnacle Polymers 1112 Polypropylene Homopolymer, Injection Molding Grade
- SABIC Innovative Plastics LNP LUBRICOMP DFL14 PC
- Nilit Nilamid B3 H ZB Unfilled, Low Temperature Impact Resistant PA6
- DuPont Performance Polymers Zytel® 101L BKB009 Nylon 66 (Unverified Data**)
- Mar-Bal MB2000-15 Thermoset Polyester Composite Molding Compound
- Intercontinental Polymers Deniers 1.5-2 Polyester Staple Fibers, Deniers 1.5 - 2
- SABIC Innovative Plastics LNP STAT-KON KEL22A Acetal Homopolymer (Europe-Africa-Middle East)
- Teknor Apex Sinvicomp SSG 6006 Polyvinyl Chloride, Flexible
- A. Schulman POLYBLAK™ 4479-01 Black Color Concentrate, 50% Carbon Black Based In LLDPE
- ArcelorMittal Dual Phase 980 LCE Y600 Very high strength steel, Cold Rolled Steel
Copyright © lookpolymers.com All Rights Reserved