Polyram PlusTek PB318G9 Nylon 6 for Injection Molding, 45% Glass-fiber Reinforced, UV Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PB318G9 Nylon 6 for Injection Molding, 45% Glass-fiber Reinforced, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
45% Glass-fiber reinforced Nylon 6, UV stabilized for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 4.9 % | 4.9 % | ISO 62 |
| Linear Mold Shrinkage | 0.0015 - 0.0040 cm/cm | 0.0015 - 0.0040 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 210 MPa | 30500 psi | ISO 527 |
| Elongation at Break | 2.8 % | 2.8 % | ISO 527 |
| Tensile Modulus | 14.2 GPa | 2060 ksi | ISO 527 |
| Flexural Strength | 280 MPa | 40600 psi | ISO 178 |
| Flexural Modulus | 11.4 GPa | 1650 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 218 °C | 424 °F | ISO 11357 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous use |
| 200 °C | 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Dielectric Strength | 65.0 kV/mm | 1650 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Hong Kun Group Pyrogallol Acid Pharmaceutical Intermediate
- Karina 42/155-RG-GE (CS) Red Color Concentrate for PVC
- Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes
- Sharadaa Ceramics HA 62D High Alumina Brick
- Cossa Polimeri ESTADIENE 3510 HT Acrylonitrile Butadiene Styrene
- Hippe PF CC 23 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Rolled Tube
- Eurostar Starflam AFR560B1 PA66, Mineral/Glass Fiber Reinforced, Flame Retardant, Injection Molding
- DSM Arnite® T04 200 PBT (European Grade)
- Carlson 904L Austenitic Stainless Steel
- DuPont Performance Polymers Zytel® FR70M30V0 NC010 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved