Polyram PlusTek PA830 Nylon 6.6, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA830 Nylon 6.6, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | DIN 53479 |
| Water Absorption | 6.7 % | 6.7 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.017 - 0.025 cm/cm | 0.017 - 0.025 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM-D785 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM-D638 |
| Elongation at Break | 50 % | 50 % | ASTM-D638 |
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ASTM-D790 |
| Izod Impact, Notched | 3.00 J/cm @Temperature 23.0 °C |
5.62 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | Continuous Use |
| >= 180 °C | >= 356 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 219 °C | 426 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | DIN 53482 |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz |
3.1 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Flint Hills H0500HN Polypropylene Homopolymer
- ICO Polymers ICOFLOâ„¢ 510-5050 500 Micron LDPE Powder
- Kolon DIAMAT® EH
- MetalTek C81100 Copper High Conductivity
- Lushan AR-5 Nylon Toughener/PA Impact Modifier
- SABIC Innovative Plastics LNP LUBRICOMP IL004 PA 6/12
- Teknor Apex APEX® 90-A472R-80-NT Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics NORYL HH180 PPE+PS
- Covestro Makroblend® DP UT6000 Polycarbonate + PBT, Impact Grade
- ExxonMobil Isopar™ E Isoparaffin Fluid
Copyright © lookpolymers.com All Rights Reserved