Polyram PlusTek PA313G43 Nylon 66 for Injection Molding, 43% Glass Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA313G43 Nylon 66 for Injection Molding, 43% Glass Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Heat stabilized, 43% Glass fiber reinforced Nylon 6.6 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 4.7 % | 4.7 % | ISO 62 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | |
| Tensile Strength, Yield | 210 MPa | 30500 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Tensile Modulus | 11.7 GPa | 1700 ksi | ISO 527 |
| Flexural Strength | 330 MPa | 47900 psi | ISO 178 |
| Flexural Modulus | 11.6 GPa | 1680 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 180 |
| Charpy Impact Unnotched | 11.0 J/cm² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| 11.0 J/cm² @Temperature -30.0 °C |
52.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 11357 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous use |
| 240 °C | 464 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- RheTech Products GC40P100-01 40% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Black
- Huntsman PE2018 Injection Molding Polyethylene (discontinued **)
- Huntsman Araldite GY 9615 Bisphenol A Epoxy Liquid Resin
- Kingfa PA6-G30 N101 30% Glass Fiber Reinforced PA6 (general purpose)
- A. Schulman FORMION™ FI 401 Ionomer
- ConocoPhillips Hydroclear® 68 Multipurpose R&O Oil, AGMA Lubricant No. 2
- Elastocon TPE Technologies Elastocon® 8138B Thermoplastic Elastomer
- Asahi Kasei Thermylene® P6-40FM-B269 40% Glass/Mineral Reinforced, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved