- Polymer Resources TP-GFMF2 Polybutylene Terephthalate, 40% Glass/Mineral Reinforced
Polymer Resources TP-GFMF2 Polybutylene Terephthalate, 40% Glass/Mineral Reinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass + Mineral Filled |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources TP-GFMF2 Polybutylene Terephthalate, 40% Glass/Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polybutylene Terephthalate, 40% Glass/Mineral ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 2.0 - 10 g/10 min @Load 2.16 kg, Temperature 250 °C |
2.0 - 10 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
| Tensile Strength, Yield | 72.4 MPa | 10500 psi | ASTM D638 |
| Flexural Strength | 121 MPa | 17500 psi | ASTM D790 |
| Flexural Modulus | 7.93 GPa | 1150 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Temperature 22.8 °C |
1.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 243 - 254 °C | 470 - 490 °F | |
| Middle Barrel Temperature | 249 - 260 °C | 480 - 500 °F | |
| Front Barrel Temperature | 254 - 266 °C | 490 - 510 °F | |
| Melt Temperature | 246 - 274 °C | 475 - 525 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 116 - 121 °C | 240 - 250 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0005 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-BOND 589-29 Conductive Epoxy
- Overview of materials for Acetal Copolymer, Unreinforced
- Momentive Performance Materials TSE399 Translucent Adhesive Sealant, Flowable
- Solvay TOLCIDE® PS 70AF 70% tetrakis hydroxymethyl phosphonium sulfate
- A. Schulman PAPERMATCH® H-5338 Specialty Masterbatch
- Buckeye Polymers BP RPP 3009 GK3 BLK Polypropylene, Glass Filled
- Cast Nylons Nycast® GF 30% Glass Filled Cast Nylon
- Austin Novel Materials Texalan® 295A Polyester-based TPU
- Aaron Industries AAROPRENE® CFPP 2030 Calcium Carbonate Filled Polypropylene
- Azdel SuperLite® SL551400-100 PP Resin Matrix / 55% Glass Fiber (4 mm Molded Thickness)
Copyright © lookpolymers.com All Rights Reserved