Polymer Resources PPX-GP4 Modified-PPO, General Purpose
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PPX-GP4 Modified-PPO, General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Modified-Polyphenylene Oxide, General Purpose, 210F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 20 - 30 g/10 min @Load 11.6 kg, Temperature 250 °C |
20 - 30 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 34.5 MPa | 5000 psi | ASTM D638 |
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Strength | 48.3 MPa | 7000 psi | ASTM D790 |
| Flexural Modulus | 1.76 GPa | 255 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Temperature -30.0 °C |
2.50 ft-lb/in @Temperature -22.0 °F |
ASTM D256 |
| 2.67 J/cm @Temperature 22.8 °C |
5.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 | |
| Charpy Impact, Notched | 1.57 J/cm² @Temperature 22.8 °C |
7.50 ft-lb/in² @Temperature 73.0 °F |
ISO 179/1eA |
| Gardner Impact | 14.1 J | 10.4 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 - 299 °C | 480 - 570 °F | |
| Middle Barrel Temperature | 260 - 304 °C | 500 - 580 °F | |
| Front Barrel Temperature | 271 - 310 °C | 520 - 590 °F | |
| Melt Temperature | 288 - 316 °C | 550 - 600 °F | |
| Mold Temperature | 71.1 - 98.9 °C | 160 - 210 °F | |
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0015 |
Users viewing this material also viewed the following:
- Oceanchem Group Melamine Polyphosphate (MPP)
- SABIC Innovative Plastics Lexan® 131 PC (Asia Pacific)
- Polymer Resources PC/TP-GP3-IM PC/Polyester Alloy, Impact Modified
- Pinnacle Polymers 1120 H Polypropylene Homopolymer, Injection Molding Grade, Nucleated, with Antistat
- MarkeTech 92-5-3 Tungsten Alloy, AMS-T-21014 Class 2
- KKPC Kuhmo GP 125H High Transparency GPPS
- Grupo Repol Dinalon® A1S25 G25 PA66 25% Glass Fiber
- SABIC Innovative Plastics LNP THERMOCOMP KF004A Acetal Homopolymer
- Fainplast Compounds GS 89/T Flexible PVC, Injection Molding for Transparent Technical Items
- A. Schulman POLYBATCH™ Grey 8218 Concentrate Based In Polyethylene
Copyright © lookpolymers.com All Rights Reserved