Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Arkema Group Orgalloy® LE 60ES03 Flexible Nylon Alloy (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon, Flexible Alloy
Manufacturer Arkema
Trade Name Orgalloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Orgalloy® LE 60ES03 Flexible Nylon Alloy (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LE series, flexible polyamide alloys: processability on PE screw, low moisture absorption, chemical resistance (no known solvents).higher in viscosity than LE 6000, suited to the blow molding of technical parts under the hood: (air intake) and to the blow molding of large volume hollow vessels.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
Water Absorption 6.4 %
6.4 %
Moisture Absorption at Equilibrium 1.8 %
1.8 %
Humidity Absorption
Melt Flow 0.30 g/10 min

@Load 2.16 kg,
Temperature 235 °C
0.30 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 37.0 MPa
5370 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal Strain; 50 mm/min
Elongation at Yield 6.0 %
6.0 %
50 mm/min
Tensile Modulus 1.20 GPa
174 ksi
1 mm/min
Tensile Creep Modulus, 1 hour 1130 MPa
164000 psi
Tensile Creep Modulus, 1000 hours 520 MPa
75400 psi
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10°C/min
Vicat Softening Point 97.0 °C
207 °F
50°C/hr; 50N
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
Copyright © lookpolymers.com All Rights Reserved