Plenco 1510 Polyester, Granular, Transfer Molded

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS , Thermoset Polyester, Mineral Filled
Manufacturer Plenco (Plastics Engineering Company)
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plenco 1510 Polyester, Granular, Transfer Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PLENCO 01510 is a mineral filled, pelletized polyester molding compound, which offers an excellent combination of electrical properties and dimensional stability. UL recognized under component file E40654. 01510 is available in black.Information supplied by Plenco.
Physical Properties Metric English Comments
Bulk Density 0.900 g/cc
0.0325 lb/in³
ASTM D1895
Density 2.01 g/cc
0.0726 lb/in³
ASTM D792
Water Absorption 0.133 %
0.133 %
ASTM D570
Linear Mold Shrinkage 0.00153 cm/cm
0.00153 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell E 78
78
ASTM D785
Tensile Strength, Ultimate 77.0 MPa
11200 psi
ASTM D638
Elongation at Break 0.55 %
0.55 %
ASTM D638
Tensile Modulus 19.8 GPa
2870 ksi
ASTM D638
Flexural Strength 119 MPa
17300 psi
ASTM D790
Flexural Modulus 19.9 GPa
2890 ksi
ASTM D790
Compressive Strength 194 MPa
28100 psi
ASTM D695
Poissons Ratio 0.284
0.284
ASTM D638
Shear Modulus 7.71 GPa
1120 ksi
Calculated
Izod Impact, Notched 0.223 J/cm
0.418 ft-lb/in
ASTM D256
Charpy Impact, Notched 0.274 J/cm²
1.30 ft-lb/in²
ASTM D256
Impact 123
123
J/m Drop Ball Impact; PLENCO
Thermal Properties Metric English Comments
CTE, linear 54.0 µm/m-°C

@Temperature 40.0 - 130 °C
30.0 µin/in-°F

@Temperature 104 - 266 °F
TMA; ASTM E831
Thermal Conductivity 0.730 W/m-K

@Temperature 100 °C
5.07 BTU-in/hr-ft²-°F

@Temperature 212 °F
ASTM E1461
Maximum Service Temperature, Air 213 °C
415 °F
Heat Resistance; ASTM D570D
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Oxygen Index 25.5 %
25.5 %
ASTM D2863
Shrinkage 0.0167 %
0.0167 %
72 hr, 120ºC; ASTM D1299
Electrical Properties Metric English Comments
Volume Resistivity 2.60e+15 ohm-cm
2.60e+15 ohm-cm
ASTM D247
Dielectric Constant 4.7
4.7
ASTM D150
Dielectric Strength 11.8 kV/mm
300 kV/in
Step by Step; ASTM D149
15.5 kV/mm
394 kV/in
Short Time; ASTM D149
Dielectric Breakdown 23000 V
23000 V
1hr 120C; ASTM D149
Dissipation Factor 0.0149
0.0149
ASTM D150
Arc Resistance 192 sec
192 sec
ASTM D495
Comparative Tracking Index 600 V
600 V
ASTM D3638