Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized |
Manufacturer | Techmer ES |
Trade Name | Plastiblend® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Techmer ES Plastiblend® PA6/6 HS L Nylon 66.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
Water Absorption | 1.2 % @Time 86400 sec |
1.2 % @Time 24.0 hour |
ASTM D570 |
Linear Mold Shrinkage, Flow | 0.018 cm/cm @Thickness 3.17 mm |
0.018 in/in @Thickness 0.125 in |
ASTM D955 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Rockwell R | 109 | 109 | ASTM D785 |
Tensile Strength, Yield | 75.8 MPa | 11000 psi | ASTM D638 |
Elongation at Yield | 90 % | 90 % | ASTM D638 |
Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm |
1.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 77.4 µm/m-°C | 43.0 µin/in-°F | ASTM D696 |
Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Unannealed; ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | Unannealed; ASTM D648 |
Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
Dielectric Strength | 21.7 kV/mm | 550 kV/in | Method A (Short-Time); ASTM D149 |