Polykemi AB SCANMID 6 B33^ E F15 Nylon 6, Glass Fiber Reinforced, Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Polykemi AB |
| Trade Name | SCANMID 6 |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANMID 6 B33^ E F15 Nylon 6, Glass Fiber Reinforced, Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Filler Content | 15 % | 15 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | With Flow; ISO 2577 |
| 0.0090 cm/cm | 0.0090 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 120 MPa | <= 17400 psi | ISO/R527 |
| Elongation at Break | 6.0 % | 6.0 % | ISO/R527 |
| Flexural Strength | <= 170 MPa | <= 24700 psi | ISO 178 |
| Flexural Modulus | 4.50 GPa @Temperature 23.0 °C |
653 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | >= 200 °C @Load 5.001 kg |
>= 392 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ U 5470A-E0083 Thermoplastic Elastomer (TPE)
- Premix Premi-Glas® 1100-10 Fiberglass Reinforced Thermoset BMC
- Polymer Resources PPX-G5 Modified-PPO, 5% Glass Reinforced
- SABIC Innovative Plastics ULTEM CRS5011 PEI (Asia Pacific)
- Stir SpA CX 3 M (PVC)
- Master Bond EP21HT High Temperature Resistant Two Component Epoxy
- Teknor Apex Telcar® TL-1996E Thermoplastic Elastomer
- ATI Wah Chang 425™ Titanium Alloy, Tubular Extruded
- PlastxWorld CEVIAN® B2704 20% GF PBT/ABS Alloy
- BASF Ultramid® B3UGM210 GR 22866 10/50% Glass/Mineral Filled PA6 FR (Conditioned)