Polykemi AB SCANMID 6 B32^ E Q30 Nylon 6, Glass Fiber Reinforced, Modified

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Polykemi AB
Trade Name SCANMID 6
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB SCANMID 6 B32^ E Q30 Nylon 6, Glass Fiber Reinforced, Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Filler Content 30 %
30 %
±2%; Polykemi
Linear Mold Shrinkage 0.0090 - 0.011 cm/cm
0.0090 - 0.011 in/in
With Flow; ISO 2577
0.0090 - 0.011 cm/cm
0.0090 - 0.011 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 80.0 MPa
<= 11600 psi
ISO/R527
Elongation at Break 15 %
15 %
ISO/R527
Flexural Strength <= 100 MPa
<= 14500 psi
ISO 178
Flexural Modulus 4.20 GPa

@Temperature 23.0 °C
 609 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.900 J/cm²

@Temperature -20.0 °C
 4.28 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
1.10 J/cm²

@Temperature 23.0 °C
 5.23 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 180 °C
356 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 100 °C
212 °F
120°C/h; ISO 75/1
Vicat Softening Point 200 °C

@Load 5.001 kg
 392 °F

@Load 11.03 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
 1200 °F

@Thickness 0.0787 in
 IEC 695-2-1