Polykemi AB SCANAMID 66 A12^ Q40 Nylon 66, Mineral Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Mineral Filled
Manufacturer Polykemi AB
Trade Name SCANAMID 66
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB SCANAMID 66 A12^ Q40 Nylon 66, Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
ISO 1183
Filler Content 40 %
40 %
±2%; Polykemi
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
With Flow; ISO 2577
0.012 cm/cm
0.012 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Hardness, Shore D 80

@Time 15.0 sec
 80

@Time 0.00417 hour
 ASTM D2240
Tensile Strength at Break <= 90.0 MPa
<= 13100 psi
ISO/R527
Elongation at Break 5.0 %
5.0 %
ISO/R527
Flexural Strength <= 135 MPa
<= 19600 psi
ISO 178
Flexural Modulus 5.00 GPa

@Temperature 23.0 °C
 725 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.500 J/cm²

@Temperature -20.0 °C
 2.38 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
0.800 J/cm²

@Temperature 23.0 °C
 3.81 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
120°C/h; ISO 75/1
Vicat Softening Point >= 230 °C

@Load 5.001 kg
 >= 446 °F

@Load 11.03 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
 1200 °F

@Thickness 0.0787 in
 IEC 695-2-1
Users viewing this material also viewed the following: