Eurostar Star L PA66 D51 PA66, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Star L |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Star L PA66 D51 PA66, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Star L PA66 D51 is a PTFE Lubricated, Unreinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.028 - 0.034 cm/cm @Thickness 4.00 mm |
0.028 - 0.034 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 71.0 MPa | 10300 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Flexural Strength | 94.0 MPa | 13600 psi | ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 34.0 kJ/m² | 16.2 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 265 °C | 509 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 265 - 275 °C | 509 - 527 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 280 °C | 518 - 536 °F | |
| Melt Temperature | 270 - 280 °C | 518 - 536 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.15 - 0.25 % | 0.15 - 0.25 % |
Users viewing this material also viewed the following:
- Momentive Performance Materials RTV60 Red Extreme High Temperature Potting/Encapsulating Compound
- Shinkong Synthetic Fibers Shinite® P305G20 PP, 20% Glass Filled
- Silberline Silvet® 210-20-J
- Solvay MIRAPOL® 550 SB Surfactant
- DuPont Teijin Films Melinex® ST329 Polyester Film, 1000 Gauge
- C.O.I.M. PLAXTER® P 42 Polymeric Plasticizer
- BASF Paliotol™ Yellow K 2270 Color Additive
- ATI Allegheny Ludlum Sealmet® 4 Controlled Expansion Alloy, UNS K94760
Copyright © lookpolymers.com All Rights Reserved