- Polykemi AB POLYfill PPH FX801020 Polypropylene Homopolymer, Glass Reinforced
Polykemi AB POLYfill PPH FX801020 Polypropylene Homopolymer, Glass Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PPH FX801020 Polypropylene Homopolymer, Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | With Flow; ISO 2577 |
| 0.012 cm/cm | 0.012 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 40.0 MPa | <= 5800 psi | ISO/R527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO/R527 |
| Flexural Strength | <= 55.0 MPa | <= 7980 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa @Temperature 23.0 °C |
435 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 205 - 260 °C | 401 - 500 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | in circulation dryer |
| 2 - 4 hour | 2 - 4 hour | in desiccant air dryer | |
| Injection Pressure | 40.0 - 110 MPa | 5800 - 16000 psi | |
| Back Pressure | 1.00 - 2.00 MPa | 145 - 290 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- Ovation Polymers Nemcon™ H PC DP105/X3 BK Polycarbonate
- PolyMirae Moplen HP553P Fiber (Staple) Grade Polypropylene
- Lanxess Durethan® BKV 325 Z H2.0 901510 Nylon 6, 25% Glass Fibers
- HP Alloys Alloy B-2, Solution Treated, 10% Cold Worked
- Shin-Etsu Silicones SV-16000U Silicone Rubber
- Styron Pulse® 2200BG ABS + PC
- Solvay Aluminum Sulfate
- Chosun Refractories A95 Special High-Density Gunning Castable
- Beijing Ranger Chem SM-602RX70 Solvent Based Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved