- Special Metals DURANICKEL® 301 (UNS N03301) Annealed and Aged Rod and Bar
Special Metals DURANICKEL® 301 (UNS N03301) Annealed and Aged Rod and Bar
| Category | Metal , Nonferrous Metal , Nickel Alloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | DURANICKEL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals DURANICKEL® 301 (UNS N03301) Annealed and Aged Rod and Bar.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tensile strength (ultimate and yield), compressive strength, hardness, and elongation values reported here are typical for Annealed and Aged Rod and Bar specifically. Other property values are typical of aged DURANICKEL® alloy 301 or the alloy in general.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.19 g/cc | 0.296 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 285 - 360 | 285 - 360 | 3000 kg |
| Hardness, Rockwell C | 30 - 40 | 30 - 40 | |
| Tensile Strength, Ultimate | 1030 - 1310 MPa | 150000 - 190000 psi | |
| Tensile Strength, Yield | 758 - 965 MPa @Strain 0.200 % |
110000 - 140000 psi @Strain 0.200 % |
|
| Elongation at Break | 20 - 30 % | 20 - 30 % | |
| Modulus of Elasticity | 207 GPa | 30000 ksi | Tension |
| Compressive Yield Strength | 948.0 MPa | 137500 psi | (0.2% Offset) |
| Poissons Ratio | 0.31 | 0.31 | |
| Shear Modulus | 76.0 GPa | 11000 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.0 µm/m-°C @Temperature 21.0 - 100 °C |
7.22 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| 14.0 µm/m-°C @Temperature 21.0 - 300 °C |
7.78 µin/in-°F @Temperature 69.8 - 572 °F |
Mean | |
| 14.7 µm/m-°C @Temperature 21.0 - 500 °C |
8.17 µin/in-°F @Temperature 69.8 - 932 °F |
Mean | |
| 16.6 µm/m-°C @Temperature 21.0 - 900 °C |
9.22 µin/in-°F @Temperature 69.8 - 1650 °F |
Mean | |
| Thermal Conductivity | 23.8 W/m-K | 165 BTU-in/hr-ft²-°F | |
| Melting Point | 1400 - 1440 °C | 2550 - 2620 °F | |
| Solidus | 1400 °C | 2550 °F | |
| Liquidus | 1440 °C | 2620 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 4.0 - 4.75 % | 4.0 - 4.75 % | |
| Carbon, C | <= 0.30 % | <= 0.30 % | |
| Copper, Cu | <= 0.25 % | <= 0.25 % | |
| Iron, Fe | <= 0.60 % | <= 0.60 % | |
| Manganese, Mn | <= 0.50 % | <= 0.50 % | |
| Nickel, Ni | >= 93 % | >= 93 % | Including Cobalt |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.010 % | <= 0.010 % | |
| Titanium, Ti | 0.25 - 1.0 % | 0.25 - 1.0 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000424 ohm-cm | 0.0000424 ohm-cm | |
| Magnetic Permeability | 9.45 | 9.45 | at 200 Oersted (15.9 kA/m). Aged at 595°C/10 h/FC. |
| Curie Temperature | <= 95.0 °C | <= 203 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1132 PC Copolymer (Europe-Africa-Middle East)
- Eastman 1870A Polyethylene (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP DX09407H PC
- Samsung Cheil Industries Starex® GR-4030 ABS, 30% Glass Filled
- Westlake Plastics Kynar® PVDF CN-F Polyvinylidene Fluoride (conductive)
- Polyram RamTough RZ220 Polycarbonate, Injection Molding
- Zotefoams Evazote® EV120CN Conductive Ethylene Vinyl Acetate Copolymer Foam
- Bohler-Uddeholm UDDEHOLM CORRAX® Precipitation Hardening Stainless Mold Steel
- Chevron Phillips Vytek™ V208A3 Enhanced LLDPE Blown Film Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved