Techmer ES Elastoblend® PA6 GF33 IM2 BK 33% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Heat Stabilized , Nylon 6, Impact Grade |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PA6 GF33 IM2 BK 33% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedAppearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Water Absorption | 1.5 % @Time 86400 sec |
1.5 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.035 cm/cm @Thickness 3.17 mm |
0.035 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 152 MPa | 22100 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 234 MPa | 34000 psi | ASTM D790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.90 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 2.08 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
3.90 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 13.9 J/cm @Thickness 3.17 mm |
26.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.4 kV/mm | 390 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Plasma Coatings 900 Surface Material
- Polimeri Europa Europrene Latice® CC 136 Carboxylated Styrene - Butadiene Copolymer
- Polimeri Europa Riblene® MM 20 Low Density Polyethylene - Injection Molding
- SABIC Innovative Plastics Lexan® HP4R PC
- ExxonMobil Exceed™ 377D60 LDPE/Hexene Tough Premium Film Resin, 0.8 mil Film (discontinued **)
- Teknor Apex UNIPRENE® 7010-87 Thermoplastic Elastomer
- ELASTO UK Dryflex® 660900S SEBS Based Material, Semi-Filled Qualities, 90A Hardness, Natural
- Arlon R37053W007 0.007" (0.178 mm) Cured Silicone Rubber with Fiberglass Substrate
- BASF N3-Amine 3-(2-aminoethylamino)propylamine
- BLUESTAR LXS 315 PPE-PS
Copyright © lookpolymers.com All Rights Reserved